BEAL INTERVENTION Military and Police Static Rope
- This military and police static rope combines lightness, durability and high strength. It is designed for covert operations and special purposes. It has many superior properties and is suitable for demanding tasks such as rescue and rappelling.
- Low elongation design: Ropes with lower elongation provide stable support during rappelling, which is particularly suitable for medium-speed rappelling operations, and can effectively improve efficiency and reduce energy loss.
- Lightweight: The unit weight of the rope is much lighter than traditional ropes, reducing the burden when carrying and using without sacrificing performance.
- High strength and durability: High tensile strength, excellent performance in handling high load and high pressure operations, ensuring safety.
- Thickened rope sheath ratio: significantly improves wear resistance, can adapt to various changeable and harsh working environments, and extends service life.
- Optimized materials and structure: The rope's internal core and external sheath are designed to be balanced, using polyamide material to ensure both flexibility and stability.
-
Exclusive management system : Each rope is equipped with a unique idN number and BCC color code to facilitate equipment tracking and ensure regular inspection and maintenance.
In order to protect the rights of consumers, this type of technical equipment involves safety issues and no returns or exchanges will be accepted (except for defects in the product itself). Please confirm before ordering!
Specification
- BEAL INTERVENTION Military and Police Static Rope Specifications
- Rope diameter : 9mm
- Rope Type: B
- Rope weight per meter: 51 g/m
- Maximum breaking strength: 2100 kg
- Figure 8 knot maximum breaking strength: 1350 kg
- Number of times it can withstand a factor 1 drop: 8
- Impact force for a drop factor of 0.3: 4 kN
- Rope slip rate: 0.3%
- Shrinkage when exposed to water: 4%
- Elongation 50/150 kg: 3.6%
- Rope leather percentage: 43%
- Rope core percentage: 57%
- Material: Polyamide
- Certification: EN 1891:1998 Type B, CE
- Origin: Madagascar
- Rope diameter : 10mm
- Rope Type: A
- Rope weight per meter: 62 g/m
- Maximum breaking strength: 2500 kg
- Figure 8 knot maximum breaking strength: 1600 kg
- Number of times it can withstand a factor 1 drop: 5
- Impact force with a drop factor of 0.3: 5.3 kN
- Rope slip rate: 0%
- Shrinkage when exposed to water: 4%
- Elongation 50/150 kg: 4.4%
- Rope leather percentage: 43%
- Rope core percentage: 57%
- Material: Polyamide
- Certification: EN 1891:1998 Type A, CE
- Origin: Madagascar
- Rope diameter : 10.5mm
- Rope Type: A
- Rope weight per meter: 65 g/m
- Maximum breaking strength: 3000 kg
- Figure 8 knot maximum breaking strength: 1800 kg
- Number of times it can withstand a factor 1 drop: 12
- Impact force with a drop factor of 0.3: 5.3 kN
- Rope slip rate: 0.8%
- Shrinkage when exposed to water: 5%
- Elongation 50/150 kg: 3%
- Rope leather percentage: 38%
- Rope core percentage: 62%
- Material: Polyamide
- Certification: EN 1891:1998 Type A, CE
- Origin: Madagascar
- Rope diameter : 11mm
- Rope Type: A
- Rope weight per meter: 73 g/m
- Maximum breaking strength: 3400 kg
- Figure 8 knot maximum breaking strength: 1950 kg
- Number of times it can withstand a factor 1 drop: 16
- Impact force with a drop factor of 0.3: 5.6 kN
- Rope slip rate: 0%
- Shrinkage upon contact with water: 1.1%
- Elongation 50/150 kg: 2.1%
- Rope leather percentage: 36%
- Rope core percentage: 64%
- Material: Polyamide
- Certification: EN 1891:1998 Type A, CE
- Origin: Madagascar
- Rope diameter : 11.5mm
- Rope Type: A
- Rope weight per meter: 78 g/m
- Maximum breaking strength: 3500 kg
- Figure 8 knot maximum breaking strength: 2200 kg
- Number of times it can withstand a factor 1 drop: 20
- Impact force with a drop factor of 0.3: 5.6 kN
- Rope slip rate: 0.5%
- Shrinkage when exposed to water: 5%
- Elongation 50/150 kg: 2.6%
- Rope leather percentage: 38%
- Rope core percentage: 62%
- Material: Polyamide
- Certification: EN 1891:1998 Type A, CE
- Origin: Madagascar